Polyester cords are more and more frequently used as reinforcement materials for rubber products in China. Nevertheless, activated polyester is still under development. Large-scale production is mostly for non-activated polyester. Dipping treatment of non-activated polyester is technically difficult. The proposal of secondary dipping process based on the traditional RFL treatment provided technical support for the application of non-activated polyester as reinforcement material in rubber industry.  The industrial cords processed from raw polyester yarns must be physically and chemically treated before used as reinforcement materials for rubber products in order to meet the intended use. For example, to realize the high transmission power and long service life of common V-belts, the elongation at specific load and the thermal stress of the cords must be adjusted. As there is no mechanical or physical adhesion between polyester cords and rubbers, their bonding depends on chemical reaction. That is to say, the cords connect with rubbers through chemical bonds after their surfaces are chemically modified. The commonly applied method is RFL (Resocinol-Formaldehyde-Latex) dipping. RFL dipping can be regarded as a “bridge” between the cords and the rubbers, which are at the two sides of the “bridge”.  Different from polyamide and rayon, there is no active radical in the polyester’s molecular structure. As polyester is an inert substance, it can hardly react with RF, and must be activated before RFL treatment. The chemical bond between rubbers and cords can be regarded as a multiple-layer structure composed of rubber layer, RFL treatment layer and activated layer.  Therefore, activation of non-activated polyester is a key step when it is applied as reinforcement material. There are normally two ways of activation:  Pre-treatment—activation of raw yarns.  Post-treatment—activation during polyester cord processing.  In western countries, chemical fibers have experienced a long-time development. Polyester is activated during the production of raw yarns, so that the pre-treatment of polyester is realized. In China, the activation pre-treatment of polyester is still under development. However, demand for polyester as reinforcement material for rubber products is higher and higher and requirement for its quality is also increasing, so that the activation of polyester depends on post-treatment of cord producers during processing.